Analytical characterization of lacquer objects excavated from a Chu tomb in China

This work presents the results of an investigation of the lacquer objects excavated from a Chu tomb in China (Warring States, 481–221 BC). This study is engaged in the examination of the methods and the materials used for the urushi coating on the objects. X-Ray fluorescence and Scanning Electron Microscopy/Energy Dispersive Using X-Ray (SEM/EDX) analyses were applied for the pigment identification. The results show that vermilion was for the red colour, while carbon black was for the black colour. Pyrolysis gas chromatography and mass spectrometry (Py-GC/MS) was applied for the characterization of the lacquer resulting that it is based on urushi. The possibility to classify the drying oil (tung or linseed oil) present in the lacquer is highlighted and discussed in this paper. Py-GC/MS with in-situ hydrolysis and methylation reagent tetramethylammonium hydroxide (TMAH) were performed on reference materials of linseed oil and tung oil as well as on the lacquer object samples. The results show that it is possible to unambiguously identify the drying oil, in our case, linseed oil was identified to retard the rate of hardening.     

浙江松阳出土南宋剔犀漆器的制作工艺及材质的研究

为了研究中国古代漆器的髹漆工艺并为漆器的保护修复提供相应的科学依据,本研究通过显微镜、显微红外光谱、扫描电镜、X射线荧光光谱、显微激光拉曼光谱等方法对浙江松阳出土南宋剔犀漆器残样的制作工艺和材质进行了研究分析。分析结果说明该漆器采用杉木作为漆胎,并在其上涂刷了以高岭土(AL2_O_3·2SiO_2·2H_2O)与动物毛发为主要成分的胎地填料(底灰)。然后分别在器物内外表面上髹饰上调制而成黑色和红色的天然生漆。将外表面红色漆膜雕刻成如意云纹,并在云纹边缘描绘黑漆线作为修饰,最后再在其上髹饰一层红色面漆。漆器红漆和黑漆层由同种天然生漆髹漆而成,但是两者采用的颜料分别为HgS和含Fe的黑色颜料。     

清雕漆描金宝座材料与工艺研究

为了了解清雕漆描金宝座的材料和工艺,对胎体制作切片进行了显微镜观察,确定了其种属;采用傅里叶红外光谱分析法分析了红漆,图谱与桐油很相近,由此可确定调漆工艺中加入了桐油。另外,结合文献,初步复原了此宝座的髹漆工艺。此研究对宝座以后的保护及清代家具及漆器的制作工艺具有参考价值。     

汉阳陵文物彩绘的结构观察及颜料成分分析

汉阳陵彩绘文物多种多样,出土时有些保存状态良好,受环境影响较小,而有些则相反。为了弄清其内部结构原因,为文物保护提供科学依据,通过显微镜观察、X-衍射分析并结合相关文献对4类彩绘文物进行了研究。研究结果表明:(1)著衣式陶俑彩绘只有一层颜料层;陶器和木马彩绘由三层构成:灰腻层、生漆有机层、颜料层;(2)漆器彩绘由2~3层漆灰-亚麻布+2层以上生漆+2~3层色漆构成;(3)陶俑和木马上的红色颜料为铁红;漆器的红色颜料是朱砂。研究建议出土时对具有生漆有机底层的彩绘即刻采取保湿措施,并采用防绉缩和加固并用的保护方法。     

SCIENTIFIC INVESTIGATIONS OF ANTIQUE LACQUERS FROM A 17TH‐CENTURY JAPANESE ORNAMENTAL CABINET

A recent restoration of a 17th‐century Japanese lacquer cabinet revealed various later treatments over the original black coating to maintain and preserve the high gloss of the oriental cabinet over the course of time and to meet changing tastes. The comprehensive investigation on a series of coating samples was executed by means of two hyphenated techniques: gas chromatography – mass spectrometry (GC–MS) and pyrolysis combined with GC–MS (Py‐GC–MS). The results showed that the original lacquer is based on urushi and linseed oil, while the past interventions are composed of sandarac, shellac and dammar. Additional microscopic studies proved the multi‐layer structure of the lacquer and the use of different pigments.     

山东青岛土山屯汉墓M162出土漆奁的髹漆工艺及相关问题研究

山东青岛土山屯汉墓出土了大量汉代漆器,大部分漆器髹涂1～2层较薄的漆,但M162出土的漆奁残片却与众不同。本研究采用数码显微镜、X射线光电子能谱、傅里叶变换红外光谱、扫描电镜能谱、X射线衍射等方法对M162出土漆奁残片的红漆层和漆灰层进行了分析研究,发现此件漆奁残片的漆灰层表面连续髹涂5层红漆,且每一层厚度均超出同时期其他墓葬出土漆器的漆层厚度,实属罕见。检视以往研究成果,这是目前发现红漆层数最多的汉代漆器标本,其制作工艺较单层髹漆更为复杂。而这种多层髹同种色漆工艺发展的原因,应当出于审美的需要,其进一步发展,或许可视为雕漆工艺的滥觞。     

Studies On Lacquerwares from Between the Mid‐Warring States Period and the Mid‐Western Han Dynasty Excavated in the Changsha Region

The development of lacquerwares reached its peak between the Warring States Period and the Han Dynasty (390–87 bc ) in the Changsha region of China. By studying excavated fragments of lacquers from this period, this paper examines the constitution of various pigmented layers, such as red, black and white layers, coloured lacquer layers, namely reddish brown or reddish orange, dark‐coloured or black, and silver lacquer layers, using non‐destructive methods. In addition, the characteristics of lacquer production techniques in Changsha are also discussed in comparison with those of other regions in China during the same period of time.     

山东日照海曲汉代夹纻胎漆器金银装饰工艺浅析

为了更好地探讨出土汉代夹纻胎漆器的金银装饰工艺,本研究运用显微镜等仪器,对山东日照海曲汉代墓地出土几件夹纻胎漆器的金银装饰工艺进行分析研究。研究发现:金饰片多镶嵌在漆灰层上的漆膜层中,银饰片和银构件多镶嵌在漆膜及漆灰层中;在金银饰与漆膜接界处有出于保护目的,且与周围图案相协调的描饰;金银装饰上的描饰与其周围的描饰图案融为一体。夹纻胎漆器的金银装饰工艺因金银饰件面,与漆膜层面高低,分为"粘贴"和"镶嵌"两类,本研究样品中暂未发现粘贴工艺。结合现代漆器装饰工艺调查结果,初步探讨了几件夹纻胎漆器金银的镶嵌工艺流程。本研究可利于汉代夹纻胎漆器金银装饰工艺的发掘、利用与传承。     

山东日照海曲墓地出土夹纻胎漆器初步分析

为进行山东日照海曲出土夹纻胎漆器的脱水保护工作,选择了19块残片,运用体视显微镜观察（OM）、X光探伤机拍摄、扫描电子显微镜（SEM）等方法,对残片的制作工艺、材质进行分析研究。分析结果表明,该批漆器是实用器;其苎麻之间无漆灰层粘结,有别于现代制作工艺;其易存水,是使其易遭受腐蚀的重要因素。本分析结果可为研究我国古代夹纻胎工艺提供素材     

“南海Ⅰ号”出水漆器残片的成分结构分析

为了用现代化学分析手段来剖析“南海Ⅰ号”漆器的髹漆工艺,以“南海Ⅰ号”出水的3片不同髹漆工艺的漆片为例,采用显微镜(OM)、X射线衍射仪(XRD)、扫描电子显微镜-能谱仪(SEM-EDS)、傅里叶红外光谱仪(FT-IR)、共聚焦拉曼光谱仪(Raman)等科学测试仪器进行研究,从髹漆的层数、显色材料的成分、漆膜的成分、漆灰的结构和成分、胎体的结构等方面来深度剖析“南海Ⅰ号”出水漆器残片的结构及制作工艺。表面显微观察显示漆片花纹精致美观,细部处理到位;截面显微观察显示剔红样品共有9层,分别是外漆5层,内漆1层,内外漆灰各1层,胎体1层;剔犀样品共7层,分别是外漆3层,内漆1层,内外漆灰各1层,胎体1层;褐漆样品共6层,分别是外漆和内漆各1层,内外漆灰各1层,内漆灰中加杂1层编织物层,胎体1层。拉曼测试结果表明3块漆片中红色显色材料为朱砂(HgS),黄色显色材料为雌黄(As_(2)S_(3)),黑色显色材料为炭黑(C)。样品中内外漆灰成分为羟基磷酸钙[Ca_(5)(PO_(4))_(3)(OH)]、石英(SiO_(2))和水合草酸钙[CaC_(2)O_(4)(H_(2)O)_(2.375)]等常见物质。漆膜的成分是生漆中添加了少量的石英颗粒,没有添加桐油作为助剂。     

长沙风篷岭汉代漆器制作工艺中淀粉胶黏剂的分析

为研究汉代髹漆工艺中是否含有淀粉粘结剂,利用淀粉粒分析方法提取了长沙风篷岭汉墓出土的漆器残片中的残留物.实验结果显示:在偏光显微镜下观察到具有十字消光特性的淀粉颗粒,粒度大小在13至25μm,且有加热糊化的现象,加热温度在60至80℃,加热时间大约在30min以内.本实验证实在汉代漆器制作过程中使用了淀粉作为粘结剂,为研究汉代漆器的制作工艺提供了新的科学方法.     

长沙风篷岭M1出土漆器检测研究

长沙市风篷岭M1出土漆器百余件,为研究该批漆器的制造工艺及保护修复方法。选取多个样品采用扫描电子显微镜、X荧光光谱仪、红外光谱仪、X射线衍射仪等进行含水率、木胎种质、漆膜和漆灰成分多项检测。结果显示:木胎漆器含水率远大于夹纻胎;木胎漆器材质有楠木、梓木等;底漆层厚度大于面漆层;漆膜中的红色颜料为HgS,黑色颜料为C,白色颜料中含Ag较高;漆灰中含有大量SiO_2和CaO。本研究成果为研究夹苎胎漆器制作工艺提供了可靠依据。     

一件清代髹漆贴金木雕观音菩萨坐像的保护研究和修复

髹漆贴金木雕属岭南地区代表性的传统木雕工艺,此类文物藏品也因此而独具特色。由于一件清代髹漆贴金木雕观音菩萨坐像存在糟朽、开裂、漆皮起翘、脱落等病害,需采取相应的修复措施。为此,在采集漆层、木胎等样品进行X射线荧光能谱、拉曼、红外光谱、切片观察等分析检测的基础上,依据分析检测结果和木雕保存现状制定实施了表面清理、菌虫防治、裂缝和残缺部位修复补全、脱落漆皮回软回贴、髹漆贴金仿卉处理等技术措施。保护处理后的木雕文物器形完整,色泽协调,形态和性质稳定,达到了预期的效果。上述分析检测手段和保护修复技术对同类文物的保护工作有借鉴作用。     

河南信阳战国楚墓出土彩席漆膜的成分、表面形态及髹漆工艺分析

河南信阳城阳城遗址M8为高等级战国晚期楚国贵族墓,该墓出土了以漆木器为主的各类文物400余件,其中尤以黑、红两色竹蔑编织而成的髹漆竹席最为精美。为开展彩漆竹席脱水保护提供基础数据,采用激光共聚焦显微镜、拉曼分析仪和傅里叶红外吸收光谱仪(FTIR)及扫描电镜-能谱(SEM-EDS)等现代分析仪器对竹席漆膜的成分及表面形态进行了分析,并在此基础上,结合传统髹漆文献资料探讨了漆膜的制作工艺。结果表明:城阳城彩席中的黑色漆膜为大漆自然显色,红色漆膜是大漆掺加朱砂调制而成;黑色漆膜表面较为平整,漆膜与胎体结合紧密,红色漆膜表面相对粗糙,结构较为疏松;竹席漆膜的厚度在0.02~0.03 mm之间,应是由大漆涂刷至少3~5次制备而成。研究结果可为下一步的彩漆竹席的脱水保护及展示提供基础数据。     

成都十二桥遗址新一村一期出土漆彩绘陶的分析研究

为了探究成都地区漆器制造历史和工艺,对2010年度成都十二桥遗址新一村一期地点出土的一批彩绘陶残片样品采用包括:加速器质谱碳十四年代测定(AMS-14C)、傅立叶变换红外光谱(FTIR)、显微镜形貌观察(OM)、显微激光拉曼(Micro-Raman)、能量色散X射线荧光(XRF)等分析方法进行了研究。结果表明这批陶器年代在西周中晚期至春秋。陶胎以易熔粘土为原料而成;彩绘层是用生漆(大漆)分别加炭黑、朱砂调和结膜而成;髹漆工艺为先髹饰黑色底漆层,然后再用含朱砂的红色颜料漆勾勒图案,黑红相间形成鲜明对比,起到良好装饰效果。这批漆陶的发现表明成都平原地区大漆工艺的使用年代可到西周中晚期。     

馆藏明代加彩木雕坐像保护前期研究

为更好地了解馆藏明代加彩木雕坐像的价值和病害情况,以期实施科学的保护和修复,利用超景深三维显微光学系统、拉曼光谱、红外光谱、X射线衍射、扫描电镜、X射线荧光能谱等分析方法对馆藏两件明代加彩木雕坐像的材质组成、制作工艺及病害情况等进行了综合分析。分析表明,两件木雕文物材质为樟科樟木属,加彩层为彩绘层,施彩工艺为先于木胎上打白灰层,而后铺一层纺织纤维,再于纤维布上涂颜料层,颜料层表面涂刷一层防护膜。其中,白灰层为石膏,纺织纤维为棉织物,所用颜料多为矿物颜料,蓝色显示物质为群青,黑色为炭黑,金色疑为铜金粉,而红色显色物质为植物染料-茜草。表面防护膜层为醇酸树脂。腐朽木材碎片和加彩层表面均有大量真菌孢子和菌丝,可以认为菌虫的侵染是引起木雕腐朽的主要因素之一。研究结果为更好地认识两件木雕文物,以及对其实施科学、有效的保护奠定了基础。     

无地仗层彩绘保护技术研究

为克服古建筑木构件上无地仗层彩绘保护的两个技术难点;彩绘加固,以防颜料脱落;防止彩绘表面易发黑,影响彩绘的色泽。本工作以常熟彩衣堂彩绘保护实例,采用先封堵木材中的纤维孔隙,再用改进的B-72配方(在配方中,加入了紫外线吸收剂,木材中油溶性成分固定剂PM-1,抗静电剂,防污剂SL等)进行化学加固处理,较好地克服了上述技术难点,为古建筑木构件上无地仗层彩绘的保护探索出了一条新途径。     

司马金龙墓出土木板漆画屏风残片的初步分析

为了解山西大同北魏司马金龙墓出土木板漆画屏风的颜料使用情况和制作工艺信息,利用Micro-Raman、FrlR、XRF、断面切片等技术,对屏风残片上的四种主要颜色(红,黑,黄,白)、红色漆底层、断面分层进行分析与鉴别,结果如下:(1)屏风所使用的颜料有朱砂、炭黑、雌黄、雄黄、石膏.(2)屏风的红色底层系由生漆与朱砂调和、结膜而成,其中可能未曾添加桐油.(3)屏风彩绘部分的颜料分层十分明确,各层的厚度相对均匀,反映出制作者较为高超的绘画技法.(4)在颜料层、木胎与红色漆底层之间的"过渡层"中,分别观察到一些白色物质.初步分析后认为,"过渡层"中白色物质为羟基磷灰石的可能性较大.颜料层中白色物质的成分和物相仍有待进一步的分析.     

馆藏元代玉泉古琴结构和髹漆工艺的科学研究

为了全面地了解古琴的制作工艺,为该类文物修复保护提供科学依据,以湖北省博物馆馆藏玉泉古琴漆膜、丝弦残片为研究对象,通过体视显微镜、电子探针、红外光谱仪(FTIR)、热裂解气相色谱串联质谱仪等多种分析方法,针对古琴的微观形貌、层次结构、组成成分及髹漆工艺等方面进行研究。结果表明,该古琴的琴身部分由木胎层、漆灰层、底漆层和色漆层构成,底漆层的运用为漆灰层和漆膜颜料层起到了很好的桥梁连接作用。在玉泉琴的制作过程中,使用了垸灰髹漆工艺,以增加古琴的机械性能与防水性,同时增加其演奏效果,其漆灰层的主要物质为骨灰。FTIR结果表明琴弦为动物性纤维;此外,提取离子技术、AMDIS加Excel漆器表征系统(ESCAPE)漆膜有机质鉴定结果表明漆膜层主要由漆液、干性油和淀粉组成,且漆液来源于三大漆树种类(Rhus verniciflua、Rhus succedanea和Melanorrhoea sp.)中的Rhus verniciflua-Urushiol(漆酚)。现代表征仪器的运用在一定程度上提取了古琴所蕴含的隐匿信息,研究结果从侧面揭示了古琴的保存状态、物质组成、层次结构和髹漆工艺等特点,为出土漆器保护修复科研工作的科学化发展提供实证支撑。     

陕西咸阳出土东汉陶器表面彩绘成分研究

为掌握陕西省咸阳市渭城区周陵镇费家村南两座东汉墓葬M17和M19出土15件陶器表面彩绘成分及保存现状,通过XRF,XRD,FTIR和SEM-EDS等分析仪器进行检测。经分析检测发现:M17出土6件陶器表面使用铅丹作为颜料,部分铅丹已转化为白色碳酸铅(PbCO_3)。M19出土陶器表面分别使用朱砂和铁红颜料,同时确定在部分器物表面使用了髹漆工艺。在M19出土的3件器物口沿处发现二氧化锡层,通过扫描电镜能谱分析和文献研究,确定其应为单质锡氧化而来,且使用锡汞齐方法镀锡,为进一步认识和理解这批器物提供了基础。