| 郑韩故城出土战国晚期铁器腐蚀产物分析 |
| |
| 引用本文： | 王淡春,罗武干,蔡全法,宋国定,王昌燧. 郑韩故城出土战国晚期铁器腐蚀产物分析[J]. 文物保护与考古科学, 2018, 30(6): 48-52 |
| |
| 作者姓名： | 王淡春 罗武干 蔡全法 宋国定 王昌燧 |
| |
| 作者单位： | 安徽博物院,安徽合肥 230071,中国科学院大学考古学与人类学系,北京 100049;中德人类演化与科技考古联合实验室,北京 100044,河南省文物考古研究院,河南郑州 450000,中国科学院大学考古学与人类学系,北京 100049;中德人类演化与科技考古联合实验室,北京 100044,中国科学院大学考古学与人类学系,北京 100049;中德人类演化与科技考古联合实验室,北京 100044 |
| |
| 基金项目： | 国家社科基金项目资助(17XKG003),国家留学基金委项目资助(201404910198),中国科学院科技史青年人才研教特别支持项目资助(2015) |
| |
| 摘 要： | 为了分析郑韩故城遗址出土战国晚期铁器的锈蚀产物类型,采用X射线衍射和金相显微观察等现代科技手段,对郑韩故城遗址内仓城铸铁遗址出土的13件样品进行综合研究。通过分析比较样品间的锈蚀程度,发现铁质文物的锈蚀机理复杂,成分多样;一些锈蚀产物中出现明显的分层,锈蚀不均;部分铁器中还存在着活性锈蚀物,其保存状态与金相组织有着密切关系。
|
| 关 键 词： | 郑韩故城 铁质文物 锈蚀产物分析 |
| 收稿时间： | 2017-05-02 |
| 修稿时间： | 2017-08-07 |
Analysis of the corrosion products of the late Warring States Period iron wares unearthed from the City Site of Zheng and Han States |
| |
| WANG Dan-chun,LUO Wu-gan,CAI Quan-f,SONG Guo-ding and WANG Chang-sui. Analysis of the corrosion products of the late Warring States Period iron wares unearthed from the City Site of Zheng and Han States[J]. Sciences of Conservation and Archaeology, 2018, 30(6): 48-52 |
| |
| Authors: | WANG Dan-chun LUO Wu-gan CAI Quan-f SONG Guo-ding WANG Chang-sui |
| |
| Affiliation: | Anhui Museum, Hefei 230071, China,Department of Archaeometry, University of Chinese Academy of Sciences, Beijing 100049, China;The Joint Laboratory of Human Evolution and Archaeometry, Beijing 100044, China,Institute of Cultural Relics of Henan Province, Zhengzhou 450000, China,Department of Archaeometry, University of Chinese Academy of Sciences, Beijing 100049, China;The Joint Laboratory of Human Evolution and Archaeometry, Beijing 100044, China and Department of Archaeometry, University of Chinese Academy of Sciences, Beijing 100049, China;The Joint Laboratory of Human Evolution and Archaeometry, Beijing 100044, China |
| |
| Abstract: | In order to determine the corrosion products of the late Warring States Period iron wares unearthed from the City Site of Zheng and Han States (Zheng Han Gucheng), 13 iron samples with corrosion products were studied using a variety of methods including X-ray diffraction (XRD) and metallographic microscopy. The results indicate complicated mechanisms, diverse components and obvious stratification of the corrosion products. Some iron wares also contain active corrosion products. This study also indicates that preservation states of iron wares have a close relationship with their metallographic structures. |
| |
| Keywords: | The City Site of Zheng and Han States Iron relics Analysis of corrosion products |