Roman blue-green bottle glass: chemical–optical analysis and high temperature viscosity modelling

Chemical analysis, optical absorption spectroscopy and mathematical modelling of high temperature viscosity have been carried out on five 1st–2nd century AD Roman blue-green bottle glass fragments from Coppergate, York. Modelled viscosities indicate remarkable consistency within the sample set studied and support the suggestion that temperatures of ∼1000–1150 °C were required to remelt these glasses and to provide suitable viscosities for forming articles. Iron redox ratios (Fe²⁺/ΣFe), analysed SO₃ contents and the absence of characteristic Fe³⁺–S²⁻ amber absorption bands suggest that melting conditions for all studied glasses were mildly, rather than strongly, reducing (estimated pO₂ ≈ 10⁻¹–10⁻⁶ bar). These furnace conditions are consistent with the effects of combustion gases and carbonaceous matter contained in the raw materials.     

Degradation processes in colourless Roman glass: cases from the Bocholtz burial

A group of Roman glass objects from the Bocholtz burial in the SW of Limburg (The Netherlands) was found to have been subject to varying degrees of degradation. Many of the 25 colourless glass objects were fragmented to pieces <0.1 cm (“sugared”), whereas the three transparent blue-green glass objects were in near-pristine state. Analyses using SEM, XRF and EDS revealed that the fragmentation was the direct result of the intense leaching of Na₂O from the glass structure and its replacement with water. The resulting gel layers with low-Na₂O contents and large amounts of water are sensitive to cracking when they dry out. Thin-walled glass appears to be less sensitive to cracking from the resulting stress than thick-walled glass. Local differences in the moisture regime during burial also influence the severity of the glass degradation. Glass with low concentrations of CaO seems to be the most sensitive to this form of degradation. The typical blue-green Roman glass is less sensitive as it generally has considerably higher concentrations of CaO.     

Pliny the Elder and Sr–Nd isotopes: tracing the provenance of raw materials for Roman glass production

In Roman and Byzantine times, natron glass was traded throughout the known world in the form of chunks. Production centers of such raw glass, active from the 4th to 8th century AD, were identified in Egypt and Syro-Palestine. However, early Roman primary glass units remain unknown from excavation or scientific analysis. The ancient author Pliny described in 70 AD that besides Egyptian and Levantine resources, also raw materials from Italy and the Gallic and Spanish provinces were used in glass making. In this study, the primary provenance of 1st–3rd century AD natron vessel glass is investigated. The use of combined Sr and Nd isotopic analysis allows the distinguishing and characterizing of different sand raw materials used for primary glass production. The isotope data obtained from the glass samples are compared to the signatures of primary glass from known production centers in the eastern Mediterranean and a number of sand samples from the regions described by Pliny the Elder as possible sources of primary glass. Eastern Mediterranean primary glass has a Nile dominated Mediterranean Nd signature (higher than −6.0 ? Nd), while glass with a primary production location in the western Mediterranean or north-western Europe should have a different Nd signature (lower than −7.0 ? Nd). Most Roman glass has a homogeneous ⁸⁷Sr/⁸⁶Sr signature close to the modern sea water composition, likely caused by the (intentional) use of shell as glass raw material. In this way, strontium and neodymium isotopes now prove that Pliny's writings were correct: primary glass production was not exclusive to the Levant or Egypt in early Roman days, and factories of raw glass in the Western Roman Empire will have been at play.     

Computer programmes for the correction of matrix effects in the XRF analysis of glass,ceramics and related silicate systems

The quantitative analysis of glass, ceramics and related silicate systems by means of energy dispersive X-ray fluorescence spectrometry is considered and problems arising from the selective absorption of X-rays in multi-element specimens are discussed. A computer programme written in FORTRAN and based upon a “semi-fundamental parameters” approach to the correction of matrix effects in glass and chemically similar materials is fully described. Model data are provided to enable the programme to be run and tested. An “empirical coefficients” computer programme for the quantitative analysis of silicate systems is outlined and the limitations of this type of programme are pointed out. The importance of adequate sample preparation prior to X-ray spectrometric analysis is stressed.     

The provenance of some glass ingots from the Uluburun shipwreck

The discovery of a Late Bronze Age trading vessel at Uluburun near Ka? off the Turkish coast offers exciting possibilities for our understanding of Bronze Age trade. On board the ship was a large consignment of glass ingots that were assumed to originate either from Mesopotamia or Egypt. This paper presents the results of major and trace elemental analyses of three deep blue and turquoise glass ingots from the Uluburun wreck, and for the first time securely demonstrates that their composition is consistent with an Egyptian origin. The compositional similarity of the glass ingots to glasses from the Mycenaean world suggests that Egypt was exporting to that region via trading ships such as that from Uluburun.     

Evidence for the trade of Mesopotamian and Egyptian glass to Mycenaean Greece

The origins of raw glass used to fashion Mycenaean beads were explored using trace elements analyzed by laser ablation ICP-TOFMS. The use of this minimally destructive technique for the in-situ analysis of these beads was ideal given that the material is exceedingly rare and thus too sensitive to make use of traditional micro-sampling (e.g., by scalpel). A wide range of trace elements were measured to compare these Greek glasses to other Late Bronze Age glass coming from Egypt and Mesopotamia. Of the eleven beads analyzed, four blue glasses colored with cobalt and two blue/green glasses colored with copper have trace element compositions consistent with an Egyptian origin of manufacture. The other five of the glasses, all colored with copper, were found to conform to the composition of Mesopotamian glass. These data are the first to demonstrate direct and clear evidence for the trade of raw glass to the Mycenaean states.     

Too little,too late: the geochemistry of a 1773 Philadelphia porcelain openwork basket

A dated (1773) openwork basket labelled “PHILADELFIA” attributed to the Bonnin and Morris factory has a lead-bearing, silicious–aluminous–calcic (S-A-C) composition that contrasts with the phosphatic (bone ash) porcelains known to have previously been made during the mid-1760s to early 1770s in what is now the United States. The basket was underfired and so contains relics of a flint (Pb) glass flux, but kiln temperatures were nonetheless sufficient for subsolidus pseudowollastonite and anorthite to have been resorbed, implying that the duration of firing (soaking) near peak kiln temperatures was insufficient to ensure thorough vitrification. During cooling, liquidus pseudowollastonite and silica polymorphs (but not anorthite) formed, showing that the melt was confined to the tridymite–pseudowollastonite cotectic above the Trd–Wol–An eutectic (1170 °C) in the SiO₂–Al₂O₃–CaO system. Rapid cooling is also indicated by quenched silica polymorphs in the relict glass particles. Although Bonnin and Morris employed some former Bow (London, c. 1743–74) workers, the S-A-C wares initially produced by this factory are compositionally distinct from the 1773 basket, which in this regard more closely resembles the body and glaze of a reputed Chelsea triangle-period (London, c. 1745–49) vessel. Regardless of how they obtained this technology, it is ironic that Bonnin and Morris chose to abandon phosphatic pastes in favour of what in Britain had become an obsolete formula.     

Opacifiers in Late Bronze Age glasses: the use of ToF-SIMS to identify raw ingredients and production techniques

Time of Flight Secondary Ion Mass Spectrometry (ToF-SIMS) is applied to the study of four samples of opaque glass of Late Bronze Age date. The technique is uniquely capable of identifying compositional heterogeneity at a sub-micron resolution within the crystalline opacifiers dispersed through homogeneous glass matrices. It is shown that this provides crucial information on the possible raw ingredients of the opacifying inclusions used, and has the potential for highlighting regional variations in the production technology involved in creating different colours of opaque glass.     

The Ethics Minefield: Issues of responsibility in learning and research

Google Glass was deployed in an Urban Studies field course to gather videographic data for team-based student research projects. We evaluate the potential for wearable computing technology such as Glass, in combination with other mobile computing devices, to enhance reflexive research skills, and videography in particular, during field research. The utility as well as the limitations of Google Glass are discussed, including its actual and potential application for teaching and data gathering purposes in the field. As such, this article constitutes one of the first instances of evaluating Google Glass as a social science research tool.     

Transition in the use of cobalt-blue colorant in the New Kingdom of Egypt

Cobalt-blue colorant was first used in the 18th Dynasty in the New Kingdom of Egypt. The source of this cobalt was cobaltiferous alum from the Western Oases of Egypt. The use of this alum, especially in glass, was suddenly limited at the end of the 18th Dynasty. There is little evidence of the production of cobalt-blue glass in the Ramesside Period (the 19th–20th Dynasties) in the New Kingdom of Egypt. In this study, we brought a portable X-ray fluorescence spectrometer to two archaeological sites located in the Memphite region and used it for onsite analyses of Ramesside cobalt blue-colored glasses and faiences. This method revealed that the compositional characteristics of the cobalt-blue colorant in these Ramesside glasses and faiences is different from the colorant derived from cobaltiferous alum used in the 18th Dynasty, based on the comparison of transition metal composition and alumina content with those of the cobalt blue-colored artifacts from the 18th Dynasty. This result suggests that a new cobalt source other than cobaltiferous alum from the Western Oases was utilized in Egypt during the Ramesside Period.