A preliminary study on the photo - degradation of printing pigments on banknotes issued during the period of the Republic of China北大核心

为了初步评价光照对民国纸币的影响,为博物馆纸币文物的展陈照明和保存提供建议,本研究选取了八枚纸币分别进行LED灯和自然光老化实验,并通过拉曼光谱仪和X射线荧光光谱仪确定了纸币样品颜料的主要成分——合成有机颜料红49:1、普鲁士蓝、铬酸铅和炭黑。通过老化前后的色差分析可知,纸币红色颜料变化最大,其他颜色变化相对较小。因此,对于民国纸币类文物,尤其是含有红色合成有机颜料的纸币文物,需要控制其光照条件以防止老化变色。     

河南荥阳官庄遗址陶范物源及制作工艺分析

Guanzhuang site is located in the west of Guanzhuang Village, Gaocun Township, Xingyang City, Henan Province. From the site, more than 3 000 pottery moulds have been unearthed, with various types, including the moulds for containers, tools, chariots, weapons, money and core, etc. According to the types and decorations of pottery moulds and the characteristics of co - existing pottery, the pottery moulds of Guanzhuang site can be divided into two periods—Phase I dating from the late Western Zhou Dynasty to the early Spring and Autumn Period, and phase TJ considered between the early and middle Spring and Autumn Period. The change of bronze ware styles from the Western Zhou Dynasty to the Spring and Autumn Period was important in the development of ancient Chinese bronze wares. Due to the lack of archaeological data, research on pottery moulds during the two - week period was still insufficient; discussion of the important issue of standardizing the sources of raw materials was also relatively weak. Environmental archaeology has relatively mature methods and practices in depositional dynamics, depositional processes and provenance tracing, which could provide new ideas for further in - depth discussions on this issue. In order to understand the material sources and craftsmanship of pottery moulds unearthed from Guanzhuang site in Xingyang, Henan Province, samples of Guanzhuang pottery moulds and natural sedimentary strata were studied using particle size analysis, XRF and petrographic analysis to give the following results. 1) The raw materials for mould - making were taken from the late Pleistocene Malan loess layer under the cultural layer of the site. The Malan loess underwent simple manual elutriation before being used to make pottery moulds. 2) A small amount of plant ash and calcium nodule powder was added during the production process of pottery moulds as an admixture to increase the high - temperature resistance. 3) The inner side of pottery mould for container was mainly made of Malan loess, while the outer one was made of a mixture of Malan loess and river sand with a blending ratio of about 7:5. Pottery moulds for various ware types had different processing techniques (e.g., moulds for containers were more refined). Besides, compared with early pottery moulds, later ones are relatively rougher, but the difference is not obvious. 4) The petrographic characteristics of double - layer container moulds indicate that there are different production processes for the inner and outer sides of mould. The inner side was made of Malan loess with finer particles—below 100 μm—as the raw material after elutriation, and there were traces of directional trimming. The outer one was made of a mixture of two parts of minerals (coarse and fine), and there was no obvious processing trace. Analysis of sample particle size is a new attempt to discuss the material sources of pottery moulds. The related discussion of mud - clarifying ponds is also helpful to understand the function of such relics and the formation process of accumulation in them. This study has important reference significance for exploring the material and craft characteristics of pottery moulds before and after the early Spring and Autumn Period in the Central Plains. © 2023, Sciences of Conservation and Archaeology. All Rights Reserved.